EPOXY BASED FLOORING PRODUCTS

EPO PR – 850

Epoxy based, two components, low viscosity and high strength primer

Description

Epoxy based, two components, low
viscosity and high strength primer product.

DESCRIPTION:
Epoxy based, two components, low
viscosity and high strength primer product.

ADVANTAGES:
Solvent free.
Easy application.
Excellent adhesion with absorbent surfaces.
Dry in a short time.
It perfectly covers the surface as
homogeneously.
Fast application
Creates a glossy film.
Resistant to general cleaning chemicals.
Can be used with all epoxy application as a
primer.

USAGE AREAS:
In and out applications,
Mall and shopping centers,
Protection cover in industrial surface
systems,
Sewage and waste facilities,
Car park and pedestrian streets,
Paper pulp and paper facilities,
Used as a primer for PU and epoxy systems

( 23 °C Temparature and 50 % for relative
humidity)
Color : Transparent
Density 20°C: 1,1 gr/cm3
Mixing Ratio : 2 / 1 weight
Flash Point : >60 °C
Application Temperature : +5°C +30°C
Heat Resistance : 121 °C Dry
Compressive Strenght : ~ 95 N / mm²
Bending Strenght : ~ 30 N / mm2
Adherance (Concrate) : >1,5 N / mm2
Shelf Life : 12 months
Consume : 0,200 – 0,500 Kg /m²
Solid Content : %100
Pot Life : 30 minutes (20°C de)
Dry Time : 6 hours
Coating Again : 8-24 hours
Total Dry : 7 days
***These values were obtained as a result
of laboratory tests, just contain finished
applications according to drying time
performance. Due to differences in
temperature and humidity values in the
construction site, the values may change.

Surface Preparation:
The surface; must be cured, dry and
durable. Loose surface mortar and such as
residues should be cleaned and reached
durable surface.
In case of the necessity the surface should
cleaned mechanically
Oil, grease, dirt, paint, salt and vomiting that
prevent adhesion should be removed.
If there are segregation, pits and fractures
on the surface, it should be repaired with
repair mortar prepared by mixing with sand
with DAYMAN EPO MORTAR, EPO –
GROUT or EPO – SAND.
Floor humidity must be max. 5 %.
On the moisture surfaces should be used
DAYMAN EPO – PR WT.

Preparation Of The Mixture:
Must be ensure that the temperature of the
product is between +15°C to +25°C before
the mixing.
Before starting A and B components, the
packages should be 400 rpm until they
reach homogeneous consistency.
It should be mixed with a speed mixer.
Mixed A + B should be mixed by a 400 rpm
low speed mixer for a few minutes until it
reaches a homogenous consistency to
make ready the primer for the application.
Remain parts of the mixing bowl and spread
part of the product should be added in to
mixing
The mixed product should be transferred to
cleaned bowl when it ready and should remixed.
Pot life of the mixed product is 25°C’de 45
minutes.
High temperatures will make shorter the pot
life of the mixed product, low temperatures
will make longer.

Application:
Ready product should be applied by roll,
brush and trowel.
Mixed product should be used before the
pot life.
The expired, gelling mixture should not be
used and should be disposed of.

The product is ready in sets and should not
be divided and the eye decision and mixed
Temperature should be between +5 °C and
+35 °C during the application.
Do not apply on surfaces that are at risk of
frost..
In addition, it should not be applied in
extremely hot, rainy or windy weather.
Ensure that the ambient and floor
temperature is between 5 ° C and 30 ° C.
Products should be stored at room
temperature 24 hours before use.
In cold weather, the reaction will slow down
due to the increase in viscosity and the
application time will be longer,
the consumption will increase. Therefore, it
is the most suitable temperature range
between 20 ° C and 25 ° C for easy
application of environment and products.
At high temperatures, the reaction and
application time interval will be accelerated.
After the application, it should be protected
from rain, water, frost and negative external
factors for 24 hours.

CLEANING OF INSTRUMENTS:
DAYMAN EPO PR 850 should be cleaned
by solvent when it wet.
DAYMAN EPO PR 850 after become dry
should be cleaned by the mechanical ways.

CONSUME:
0,200 – 0,500 kg / m² depending on surface
absorbency.

PACKING:
A+B component: 18, 00 kg
Pallet 120×80
Qty on pallet 18 set – 36 Bin

COLOR:
Transparent-Xanthic

SHELF LIFE:
1 year from the production date under
proper storage conditions.
Opened packages should be kept tightly
closed.
Wear suitable protective clothing, protective
gloves, goggles and mask during
application.

SAFETY RECOMMENDATIONS:
1 year from the production date under
proper storage conditions.
Should be storage between the temperature
of the DAYMAN EPO – PR 850 5 °C with
25° C

LIMITATIONS OF LIABILITY:
The information in this technical data sheet
is given according to technical information,
experience and test result.
As GENERALTÜRK A.Ş. cannot control the
usage of the product that used under which
kind of conditions, it does not accept any
responsibility for the application result and
does not guarantee it.
The product suitability for the product user
should be tested and decided accordingly.
All products should be considered in the
advice of those technical knowledge and
equipment.
GENERAL TURK A.Ş can not accept any
resposibility that occures because of missuse,it only responsible for the written
suggestions that shows the products where
and how use.
GENERALTÜRK A.Ş. It may change the
properties of its products without
announcement.
The technical data sheet is valid until the
next time it is printed and all previous
technical data sheets invalidate the
description

Click to view the Technical Sheet.