EPO PR FK – 864
Epoxy based, moist tolerated, two components, low viscosity, high adherence and high
strength primer product
Description
Epoxy based, moist tolerated, two
components, low viscosity, high adherence
and high strength primer product.
DESCRIPTION:
Epoxy based, moist tolerated, two
components, low viscosity, high adherence
and high strength primer product.
ADVANTAGES:
Solvent free.
Easy application.
Moist tolerated.
Excellent adhesion with absorbent surfaces.
Dry in a short time.
It perfectly covers the surface as
homogeneously.
Fast application
Creates a glossy film.
Resistant to general cleaning chemicals.
Can be used with all epoxy application as a
primer.
USAGE AREAS:
In and out applications,
Mall and shopping centers,
Protection cover in industrial surface
systems,
Sewage and waste facilities,
Car park and pedestrian streets,
Paper pulp and paper facilities,
Used as a primer for PU and epoxy
systems,
( 23 °C Temparature and 50 % for relative
humidity)
Color : Xanthic
Density 20°C : 1,1 gr/cm3
Mixing Ratio : 2 / 1 weight
Flash Point : > 60 °C
Application Temperature : +5°C +30°C
Heat Resistance : 121 °C Dry
Compressive Strenght : ~ 95 N / mm2
Bending Strenght : ~ 30 N / mm2
Adherance (Concrate) : >1,5 N / mm2
Shelf Life : 12 months
Consume : 0,200 – 0,500 Kg /m²
Solid Content : %100
Pot Life : 30 minutes (20°C de)
Dry Time : 6 hours
Coating Again : 8-24 hours
Total Dry :7 days
***These values were obtained as a result
of laboratory tests, just contain finished
applications according to drying time
performance. Due to differences in
temperature and humidity values in the
construction site, the values may change.
Surface Preparation:
The surface; must be cured, dry and
durable. Loose surface mortar and such as
residues should be cleaned and reached
durable surface.
In case of the necessity the surface should
cleaned mechanically
Oil, grease, dirt, paint, salt and vomiting that
prevent adhesion should be removed.
If there are segregation, pits and fractures
on the surface, it should be repaired with
repair mortar prepared by mixing with sand
with DAYMAN EPO MORTAR, EPO –
GROUT or EPO – SAND.
Floor humidity must be max. 5 %.
Should be repaired with the mortar that
mixed with sand.
Preparation Of The Mixture:
Must be ensure that the temperature of the
product is between +15°C to +25°C before
the mixing.
Before starting A and B components, the
packages should be 400 rpm until they
reach homogeneous consistency.
It should be mixed with a speed mixer.
Mixed A + B should be mixed by a 400 rpm
low speed mixer for a few minutes until it
reaches a homogenous consistency to
make ready the primer for the application.
Remain parts of the mixing bowl and spread
part of the product should be added in to
mixing
The mixed product should be transferred to
cleaned bowl when it ready and should remixed.
Pot life of the mixed product is 25°C’de 45
minutes.
High temperatures will make shorter the pot
life of the mixed product, low temperatures
will make longer.
Application:
Ready product should be applied by roll,
brush and trowel.
Mixed product should be used before the
pot life.
The expired, gelling mixture should not be
used and should be disposed of.